What is the difference between zinc-plating & galvanising? And which will be best for your farm fences?
Browse our range of hot-dip galvanised gate hardware. Our range is high-quality, reliable, and best of all—fast & easy to install.
Galvanisation is when a protective zinc coating is applied to steel or iron, to prevent rusting.
The most common method is hot-dip galvanising. This is when metal parts are fully submerged in a bath of molten zinc.
Zinc plating (also known as electro-galvanising) is a process where zinc is applied by using a current of electricity. While is does provide some rust protection, its thinner coating is not as rust resistant as hot dip galvanising. Its main advantage is it is cheaper and easier to weld.
Be careful when choosing your product! The fact that it says ‘galvanised’ doesn’t mean it’s ‘hot dip galvanised’. Electro-galvanising is another term for zinc plating. So when you see ‘galvanised’ use your newly acquired knowledge to make sure it is hot dip galvanised and not electro-galvanised.
Hot dip galvanising or zinc plating can be used on anything from small nuts and bolts to large beams for buildings. The steel is put in a big bath, where the coating is applied.
If it’s galvanised, it will be dull grey and a little rough. A zinc plated product will be shiny and smooth. A hot dip galvanised product has the best protection against rust, even though it’s a bit ugly.
Whether the steel is to be hot dip galvanised or zinc plated it is prepared in a similar way. The steel is cleaned to remove all oils, paint, grease, mill scale (small flakes of metal) and rust in a bath of acid.
Steel, when being hot dip galvanised is dipped into a 450°C bath of molten liquid zinc. The steel and the liquid zinc bond together because of the high temperature. The steel and the zinc become one.
Zinc plating, on the other hand, is immersed in a cold chemical solution of zinc and uses an electrical current to apply a layer of zinc. The thickness of the coating is measured in microns or micrometre’s (μm). Zinc plating requires a minimum thickness of 5μm (.005mm) and a maximum of 25μm (.025mm). It would become too technical and expensive to coat the steel any thicker than this.
Hot dip galvanising requires a minimum thickness of 45μm (.045mm) and goes beyond 100μm (.1mm)
A product that is hot dip galvanised will have a thicker coating, meaning it will last far longer. Hot dip galvanised coatings give superior protection against corrosion.
The images below show that zinc plated gate hardware will rust over time. This puts more strain on your hinges, stops your gate from swinging smoothly, and looks unsightly.
Selecting the right gate hardware for your conditions is extremely important. Choosing the right material, especially if you're in a coastal area, where corrosion occurs faster than inland areas, will save you time and money. The last thing you want to do is install all your fencing, only to find it has rusted quickly and needs to be replaced. While is is particularly important in coastal areas, the second row of images above are from a central Victorian property, quite a distance from any corrosive sea air, and the zinc plated gate hardware has still rusted.
We are all ears!
Interested in purchasing our products?
Our products are stocked by a variety of stores all over Australia including stores in New South Wales, Queensland, Victoria, Tasmania, South Australia, Western Australia, Northern Territory and the Australian Capital Territory,
Replace Your Damaged Fences with Fire Resistant Farm Fencing16 Oct, 2019
Cost Of Improving Your Farm Fences Before Selling10 Oct, 2019
Bolt-On Adjustable Round Post Hinge Set FG6 Installation (Video)21 Nov, 2018
Exclusion Fencing Guide: How To Reduce The Impact From Feral Animals & Pests20 Apr, 2018
Rural Fencing Tips: Your Detailed Farm Fence Post Spacing Guide13 Apr, 2018
Rural Fencing Contractors14 Mar, 2018
Strainer Post Installation: Handy Facts & FAQs To Secure Your Fence18 Jan, 2018
Low-Loc Gate Kit & Screw-In Ring Latch Installation (Video)